资料描述

【英文标准名称】: Standard Test Method for Density of Powder Metallurgy (PM) Materials Containing Less Than Two Percent Porosity
【原文标准名称】: 孔隙度小于2％的粉末冶金材料密度的标准试验方法
【标准号】: ASTM B311-2008
【标准状态】: 现行
【国别】: 美国
【发布日期】: 2008
【实施或试行日期】:
【发布单位】: 美国材料与试验协会(US-ASTM)
【起草单位】: B09.11
【标准类型】: (Test Method)
【标准水平】: ()
【中文主题词】:
【英文主题词】: cemented carbides; density; hard metals; metal injection molded (MIM) parts; powder metallurgy (P/M); powder forged (P/F) parts; powder metallurgy
【摘要】: For PM materials containing less than two percent porosity, a density measurement may be used to determine if the part has been densified, either overall or in a critical region, to the degree required for the intended application. Density alone cannot be used for evaluating the degree of densification because chemical composition and heat treatment affect the pore-free density. For cemented carbides, a density measurement is normally used to determine if there is any significant deviation in composition of the carbide grade. For straight tungsten carbide-cobalt grades, the relationship is straightforward. For complex carbide grades (for example, grades containing tantalum carbide or titanium carbide, or both, in addition to tungsten carbide-cobalt), the situation is more complicated. If the measured density is beyond the specified limits, the composition is outside of the specified limits. A measured density within the specified limits does not ensure correct composition; compensation between two or more constituents could result in the expected density with the wrong composition. Density alone cannot be used for evaluating a cemented carbide grade.1.1 This test method covers the determination of density for powder metallurgy (PM) materials containing less than two percent porosity and for cemented carbides. This test method is based on the water displacement method. Note 18212;A test specimen that gains mass when immersed in water indicates the specimen contains surface-connected porosity. Unsealed surface porosity will absorb water and cause density values higher than the true value. This test method is not applicable if this problem occurs. 1.2 With the exception of density values, for which the g/cm3 unit is the industry standard, the values stated in SI units are to be regarded as the standard. Values in inch-pound units are shown in parentheses and result from conversion in accordance with IEEE/ASTM Standard SI 10. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
【中国标准分类号】: H16
【国际标准分类号】: 77_16
【页数】: 4P.;A4
【正文语种】: 英语